Аморфные поли-альфа-олефины: от побочного продукта к целенаправленному синтезу.

Amorphous poly alpha olefin (APAO; also known as atactic poly alpha olefin) is a commodity chemical used in multiple applications.

In the mid to late 1950s, atactic polypropylene (APP) was a by product of the synthesis of isotactic polypropylene (iPP) using first and early second generation Ziegler–Natta catalysts (Z N catalysts), which typically produced about 10 15 wt% of APP. Polymerization reactions using those catalysts were based on solution processes that simplified the elimination of the APP due to solubility differences. In other processes, such as slurry or suspension, the APP had to be eliminated from the isotactic fraction by washing/extracting the polypropylene product with hydrocarbon solvents. With the development in the 1980s of more active and stereospecific supported Z N catalysts, the proportion of atactic polymer to crystalline isotactic polypropylene in the polymers produced was substantially reduced, to typically less than 2 or 3 wt%. Therefore, the polypropylene product generally did not require additional purification steps to remove the atactic or low crystalline fraction. This meant that the APP supply from polypropylene plants using standard first and early second generation Z N catalysts decreased as commercial plants adopted the new catalysts. Little by product APP was thereafter produced. Because APP is a by product, it frequently has broad product specifications Starting in the late 1970s and the early 1980s, several chemical companies identified the need to have an APP like polymer produced to tight specifications. This type of polyolefin became known as on purpose APAO, or just APAO, or APO. APAO synthesis and manufacture has been accomplished by properly designing the process of synthesizing the amorphous polyolefin, specifically, by the proper choice of catalyst system and the use of olefinic co monomers. This process results in products with defined properties, such as melt viscosity, softening point, needle penetration, open time and tensile strength.

The amorphous polyalphaolefins are synthesized by a catalyst system based on a Z N supported catalyst and an alkyl aluminum co catalyst. The polymerization process produces a mostly amorphous polymer with low crystallinity. Crystallinity depends on the catalyst system and on the use of co monomers.